Filmes finos de carbono amorfo hidrogenado (a-C:H) têm sido depositados na superfície de materiais para melhorar propriedades mecânicas, ópticas e químicas. Nesse estudo, foi empregado o sistema de deposição química assistida por plasma (PECVD) para sintetizar filmes de a-C:H com fases DLC (tipo diamante) e PLC (tipo polimérico). As pressões parciais de acetileno em argônio foram variadas e as estruturas dos produtos analisadas pela técnica de espectroscopia de reflexão-absorção no infravermelho (IRRAS) e Raman. Além disso, a morfologia e as espessuras dos filmes foram determinadas por microscopia de força atômica (AFM) e perfilometria, respectivamente.

Hydrogenated amorphous carbon (a-C:H) thin films were synthesized on the surface of materials to improve mechanical, optical and chemical properties. In the present study, plasma enhanced chemical vapor deposition (PECVD) was performed to produce a-C:H films with PLC (polymer like carbon) and DLC (diamond like carbon) phases. The influences of the acetylene partial pressure and chamber pressure on the chemical structures of the products were evaluated by infrared reflection absorption spectroscopy (IRRAS) and Raman spectroscopy. Moreover, the morphology and thickness of the films were investigated by atomic force microscopy (AFM) and profilometry, respectively.

Os resíduos sólidos urbanos (RSUs) são atualmente um dos maiores problemas ambientais, por serem gerados em grande quantidade e ocuparem extensos espaços por um longo período, resultando na diminuição do tempo de vida útil dos aterros sanitários. Os polímeros constituem um grande percentual da composição do RSUs, sendo que as embalagens plásticas contribuem com maior volume e massa. Apesar da reciclagem de polímeros estarem se consolidando no Brasil, graças ao seu mercado ascendente e promissor, existem ainda restrições quanto a sua utilização em contato com alimentos devido aos eventuais processos de migração de contaminantes que podem ocorrer da resina reciclada para o alimento. Por outro lado, dados recentes do setor indicam que a maior parte do consumo de resina virgem é destinada, justamente, para o mercado de embalagens alimentícias. Assim, o desenvolvimento e o gerenciamento de tecnologias que possibilitem o retorno destes materiais a sua aplicação original é de grande importância para sociedade contemporânea. Em um panorama geral, este trabalho aborda as exigências e limitações do uso de polímeros reciclados para contato com alimentos.

Municipal solid waste has recently become one of the severest environmental problems. This is because it is generated on a large scale and occupies large spaces for long periods resulting in a decrease in the useful life of landfills. Polymers comprise a large percentage of municipal solid waste and polymer packaging is responsible for the large mass and volume amount. Despite the consolidation of polymer recycling in Brazil, due to the promising and growing market, there are still restrictions concerning to its application for food contact due to eventual migration process that might occur from the recycled resin into the food. On the other hand, recent data of the sector indicates that food packaging market is responsible for the highest consumption of the produced amount of virgin polymers. Therefore the development and management of technologies that facilitate the returning of these materials to their original purpose are urgently needed. In general, this article focuses on the needs and limitations of the return process of the recycled polymer to the food contact package.

Neste trabalho, as propriedades reológicas de blendas de PEAD virgem e PEAD reciclado, em diferentes porcentagens, foram avaliadas em regime permanente, transiente e dinâmico de cisalhamento utilizando-se reometria cone-placa e reometria capilar. Embalagens de PEAD pós-consumo foram coletadas e submetidas aos processos básicos de recuperação de plásticos: lavagem, moagem e secagem. Formulações, previamente estabilizadas, contendo 0, 25, 50, 75 e 100% de material reciclado, adicionado à resina virgem, foram reprocessadas por extrusão e posterior injeção. Das medidas das propriedades reológicas foi possível concluir que a incorporação de material reciclado proveniente de resíduo pós-consumo à resina virgem promove, neste caso, uma diminuição da massa molar e aumento na sua distribuição. Além disso, um estudo das propriedades reológicas permite a predição de seu comportamento frente ao processamento de resinas recicladas pós-consumo.

In this study, the incorporation of a high density polyethylene (HDPE) resin in a virgin resin was assessed by means of its rheological properties with the use of shear steady, transient and dynamic flows using cone and plate and capillary rheometry. HDPE post-consumer packaging was collected and submitted to a basic process of plastic recovering: washing, grinding, and drying. The formulations had 0, 25, 50, 75 and 100% of recycled material added to the virgin resin, and were reprocessed by extrusion and injection molding with stabilization. From the rheological measurements it was concluded that the incorporation of the recycled material from post-consumer packaging to the virgin resin produced, in this case, a decrease in the molar mass and an increase in its distribution. Therefore, the rheological properties allow the prediction of the processing behavior of post-consumer recycled materials.